无卤素红胶

成  份    Composition

环氧树脂： Epoxy resin

外 观         Appearance

红色糊状：  Paste/red-colored

比 重   Specific gravity

1.20

粘 度  Viscosity at 25℃,5rpm

280,000mPa·S(280,000cps)

摇变性指数  Thixotropy index

6.9(1rpm/10rpm)

接着强Adhesive Strength  2125C

Mini-mold tr

SOP·IC 16P                              

44N(4.5kgf)0.2mgr twin

45N(4.6kgf)0.3mgr twin

92N(9.4kgf)0.8mgf single×2

电气特性 Electric Property

体积阻抗系数Volume resistance

绝缘阻        Insulation resistance

初期值           Initial value

处理后*           After treating*

介电常数       Dielectric constant

介电正接    Dielectric loss tangent

3.6×10¹⁶Ω·cm    JIS K6911

1.2×10¹⁴Ω                JIS Z3197

1.2×10¹²Ω               

3.12/1MHZ      JIS K6911

0.012/1MHZ     JIS K6911

保存条件    Preservation condition

10℃以下的冰箱保存

To be strictly kept at less than

10℃ in refrigerator

包装方式

Package styles

容量

Contents

包装单位

Pack.Unit

点胶机设备厂商

Applicable Dispenser Makers

1．圆柱筒

300ml

5Pcs.

For our filling machines only

2．Syringe A type

点胶管

30cc

12Pcs.

KYUSHU MATSUSHITA,SANYO,TDK,

CITIZEN,TOSHIBA,SONY,CKD,

NITTO KOGYO,YAMAHA

3．Syringe B type

30cc

12Pcs

FUJI

4．Syringe C type

30cc

12Pcs

Panasert(Long:Mo)

5．Syringe D type

20cc

12Pcs

Panasert(Short:MK,MV)

6．Syringe E type

10cc

12Pcs

TENRYU,CASIO,JUKI,OKANO

1.       Much lower temperature curing is aimed at amd is practically possible.

2.       Very good stable curing shapes without stringing and slumping are achieved at super high speed dispensing and very amall dots.

3.       stable adhesive strength can be obtained with a variety of SMD.

4.       Long-term preservation stability is expected.

5.       High heat-resistivity and excellent electric properties are possessed.

1．  容许低温度硬化。

2．  尽管超高速涂敷、微少量涂敷仍可保持没有拉丝，塌陷的稳定形状。

3．  对於各种表面粘着零件，可获得安定的接着强度。

4．  储存安定性优良。

5．  具有高度耐热性和优良的电气特性。

○Recommended curing condition:Over 150 sec after PCB’s surface temperature has reached 110℃.or over 120 sec after PCB’s surface temperature has reached 120℃.

○When the higher curing temperature and the longer curing time,the stronger adhesive strength can obtained.We would suggest you to search out an optimum curing condition,for the temperature exerterd on the adhesive may occasionally vary according to the size,material,etc.of component parts mounted on PCBs.

固化条件

○建议固化条件是PCB板表面温度达到110℃后150秒以上，或者是达到120℃后120秒以上。

○固化温度越高，且固化时间越长，可获得更高的粘接强度，依PCB板上装着元件材质、大小不同而实际附加于接着剂的温度会有所不同，因此请依据实际生产情况找出最适合的固化条件。

○Adhesive should be preserved in refrigerator(below  5±3℃)to keep on its quality.

○Before processing,the adhesive should be taken out from the refrigerator for de-freezing about 4 hours until it reaching the room temperature.

○The bottom of printing screen should be cleaned timely for good printing shape.

○Toluene or ethyl acetate is possible to use for cleaning up this adhesive.

使用方法

○为使接着剂的特性发挥最大效果，请务必放置于冰箱（5±3℃）保存。

○使用前请务必提前4小时从冰箱取出，待红胶恢复至室温后使用。

○为获得良好印刷成形，请及时清洁钢网底部。

○对红胶的洗涤可使用甲苯，醋酸乙酯。

○Warranty:6Months.

○Store adhesive in a refrigerator keeping the temperature at 5±3℃

○This product may cause skin irritation to sensitive personnel.

○In case ET-T984 gets in touch with skin,wash it thoroughly with soap and water.

○In case of eye contact,wash out with clean water and consult a medical doctor immediately.

○保证期：6个月。

○请务必将本品保存在5±3℃的冰箱内。

○如果有过敏性体质的人，直接接触皮肤有时会引起皮肤过敏，因此请注意。

○误沾皮肤时，请立即用肥皂水清洗。

○进入眼睛时，请尽速以清水冲冼干净，立即接受医生的诊察。